Prob.8:[2.63] A standard tension test is used to determine the properties of anexperimental plastic. The test specimen is a 16 mm diameter rod and it issubjected to a 3.2 kN tensile force. Knowing that an elongation of 11 mmand a decrease of diameter of 0.625 mm are observed in a 125 mm gagelength, determine the modulus of elasticity, the modulus of rigidity, andPossion's ratio of the material.P16 -mm diameter125 mmP'

Answered: Image /qna-images/answer/3a387c09-bc83-4853-a941-018d08b37859.jpg

[2.63] A standard tension test is used to determine the properties of an experimental plastic. The test specimen is a 16 mm diameter rod and it is subjected to a 3.2 kN tensile force. Knowing that an elongation of 11l mm and a decrease of diameter of 0.625 mm are observed in a 125 mm gage length, determine the modulus of elasticity, the modulus of rigidity, and Possion's ratio of the material. P 16 -mm diameter 125 mm P'

[2.63] A standard tension test is used to determine the properties of an experimental plastic. The test specimen is a 16 mm diameter rod and it is subjected to a 3.2 kN tensile force. Knowing that an elongation of 11l mm and a decrease of diameter of 0.625 mm are observed in a 125 mm gage length, determine the modulus of elasticity, the modulus of rigidity, and Possion's ratio of the material. P 16 -mm diameter 125 mm P'

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A standard tension test is used to determine the properties of anexperimental plastic. The test specimen is a 15 mm diameter rod and it issubjected to a 3.2 kN tensile force. Knowing that an elongation of 11 mmand a decrease of diameter of 0.625 mm are observed in a 120 mm gagelength, determine the modulus of elasticity, the modulus of rigidity, andPossion’s ratio of the material.
Callister Problem 6.20: A brass alloy is known to have a yield strength of 275 MPa, a tensile strength of 380 MPa, and an elastic modulus of 103 GPa. A cylindrical specimen of this alloy 12.7 mm in diameter and 250 mm long is stressed in tension and found to elongate 7.6 mm. On the basis of the information given, is it possible to compute the magnitude of the load that is necessary to produce this change in length? If so, calculate the load. If not, explain why.
A circular aluminum alloy [E = 70 GPa; a = 22.5 x 10-6/°C; v = 0.33] pipe has an outside diameter of 245 mm, a wall thickness of 15 mm, and a length of 4.5 m. The pipe supports a compressive load of 610 kN. After the temperature of the pipe drops 49°C, determine: (a) the axial deformation of the pipe. (b) the change in diameter of the pipe. Answer: (a) 8 = i AD= i mm mm
For the antenna tower shown, it is supported in its upright position by four high tensile wires. Given specifications of the tensile wire: E = 200 GPa, diameter = 12 mm. If a = 6 m and b = 8 m Which of the following most nearly gives the elongation (in mm) of wire AD if F = 10 kN.
Problem 1.1. A rod 150 cm long and of diameter 2.0 cm is subjected to an axial pull of 20 kN. If the modulus of elasticity of the material of the rod is 2 x 105 N/mm2 ; determine : (i) the stress, (ii) the strain, and: (iii) the elongation of the rod:
Help
Young's modulus of elasticity and Poisson's ratio of a material are 1.25 x 105 MPa and 0.34 respectively. The modulus of rigidity of the material is: (a) 0.4025 x 105 MPa (c) 0.8375 x 105 MPa (b) 0.4664 x 105 MPa (d) 0.9469 x 105 MPa
A 14 mm diameter rod of an experimental plastic is subjected to a tensile force of magnitude P 150 mm gage length and there is a decrease in diameter of 0.4 mm, determine the modulus of elasticity, Poisson's ratio, and the modulus of rigidity (a.k.a shear modulus) for the material. 4.2 kN. Knowing that the elongation is 7 mm over a