9.11. In Fig. P9.11 is shown a cast iron frame with a U-shaped cross section. Theultimate tensile strength of the case iron iso = 320 MPa.70 mm300 mm-180 mm-240 mm-C60 min30 mm**30 mmFigure P9.11(a)Determine the maximum value of P based on a factor of safety SF =4.00 which is based on the ultimate strength.(b)Neglecting the effect of stress concentrations at the fillet at the junc-tion of the web and flange, determine the maximum radial stress whenthis load is applied.(e) Is the maximum radial stress less than the maximum circumferen-tial stress?

The ultimate tensile strength of the cast iron is .The factor of safety is .

Answered: In Fig. P9.11 is shown a cast iron…

In Fig. P9.11 is shown a cast iron frame with a U-shaped cross section. The ultimate tensile strength of the case iron is o, = 320 MPa.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A tensile test was conducted on a mild steel& the following data was obtained as follows. Diameter of the steel bar = 3 cm,Gauge length of the bar = 20 cm. Load at elastic limit = 250 kN . Extension at a load of 150kN = 0.21 mm . Maximum load = 380 kN . Total extension = 60 mm . Diameter of the rod at failure = 2. 25 cm Determine: (a) Young’s modulus (b) stress at elastic limit (c)the percentage of elongation (d) Percentage decrease in area.
In a standard tensile test a steel rod of 7/8 in. in diameter is subjected to a tension force of 17 kips. Determine the ratio of the shear modulus to the modulus of elasticity of a material whose Poisson's ratio is 0.25.
QI (a) A tensile stress is to be applied along the axis of a cylindrical steel rod that has a diameter of 7.5 mm. Given the Poisson's ratio, v is 0.30 and the modulus of elasticity, E of the steel is 207 GPa. Determine the magnitude of the load required to produce a 2.5 x10³ mm change in diameter if the deformation is entirely elastic. (b) Referring to the tensile test data tabulated in Table 1, answer the following questions: i. Select with justification the material that will experience the greatest percent reduction in area. ii. Select with justification which material is the strongest. Table 1. Tensile stress-strain data for several hypothetical metals Material Yield Tensile Strain at Fracture Elastic Strength Strength Fracture Strength Modulus (МРа) (MPa) (MPa) (GPa) A 310 340 0.23 265 210 100 120 0.40 105 150 C 415 550 0.15 500 310 D 700 850 0.14 720 210 E Fracture before yielding 650 350
A sample test rod made of a ferrous material of 0.5 in. diameter was tested for tensile strength with the gauge length of 2.5 in. The following observations were recorded: Final length = 3.15 in; Final diameter = 0.275 in; Yield load = 7650 lb. and Ultimate load = 10375 lb. (a) Calculate: 1. yield stress, 2. ultimate tensile stress, 3. percentage reduction in area, and 4. percentage elongation. (b) What specific material, if any, is similar to this tested rod? Refer to AT7 and AT8. (c) This same material is then used as a tension member 55 inches long and is subjected to a maximum load of 6000 lb, repeated but not reversed. (d) Solve part (c) if the total elongation is not to exceed 0.025 in.? 1. %3D
Q3b. The stress-strain characteristic curves for materials A, B and C are shown below. Which one statement most accurately describes the relative toughness and ductility for materials A, B & C? Material A Material B Material C Strain Select one: a. Material A has low toughness, Material B has high ductility and Material C has low toughness. b. Material A has high toughness, Material B has low ductility and Material C has low toughness. c. Material A has low ductility, Material B has low toughness and Material C has low toughness. d. Material A has high ductility, Material B has low toughness and Material C has high toughness. Stress
Scenario. Three specimen of D12 rebar was subjected to a Tensile Test. Using a steel density of 8000Kg/cu.m. With the following result specimen 1 specimen 2 M=0.895 kg M=0.89 kg L=98 cm L=99 cm Load at yield strength= 5000 kg Load at ultimate =8600 kg Gauge length after test=21.5 cm Load at yield strength= 5000 kg Load at ultimate =8600 kg Gauge length after test=21.6 cm specimen 3 M=0.897 kg L=100 cm Load at yield strength= 5010 kg Load at ultimate strength=8590 kg Gauge length after test=21.6 cm specimen Yield strength Yield strength Ultimate strength Ultimate strength STRAIN based on actual based on 12mm based on actual based on 12mm diameter (MPa) diameter (MPa) diameter (MPa) diameter (MPa) 1. 2. average
An engineer determines that a 32 cm long rod of 1020 grade steel will be subjected to a tension of 40 kN. The following two design requirements must be met: the stress must remain below 120 MPa, and the rod must stretch less than 0.135 mm. Determine an appropriate value for the rod's diameter to meet these two requirements. (Round up to the nearest millimeter when reporting your answer.) mm
4. A mild steel material is tested using universal testing machine & the following data was obtained as follows. Diameter of the steel bar = 5 cm, (ii) Gauge length of the bar = 150 cm, Load at elastic limit 650 kN (iv) Extension at a load of 350kN = 0.25 mm, Maximum load = 500 kN (vi)Total extension failure = 1.5 cm. Determine: (a) Young's modulus elastic limit (c) the nercentage of elongation in area. %3D = 5.5 cm, Diameter of the rod at (b) (d) Percentage decrease stress at
The table below shows the deformation data that resulted from applying a pure tensile load to a brass alloy rod with an initial length of 30 mm and a diameter of 10 mm. This rod was subjected to necking and beyond necking deformation. The data at fracture is shown in the last row. Applied Load (N) Length (mm) Diameter (mm) 75,100 33.8 68, 250 34.9 50,200 35.7 6.7 Solve for the TRUE STRESS/ES and TRUE STRAINS. 8.3 7.8
A bar with a cross-sectional area of 1300 mm, length of 1.5 m, modulus of elasticity of 70 GPa, and coefficient of thermal expansion of 24 x 10-6/°C is rigidly constrained on both ends. Determine the stress, in MPa, if the temperature of the bar increases by 13 °C. Add your answer
2. Ten point load tests are carried out on cylindrical specimens of a sedimentary rock with 30 mm diameter, as shown in the figure. 50 mm The failure loads of these tests are equal to: 3.2, 4.1, 3, 3.8, 2.9, 4.2, 3.5, 3.6, 3.5 and 4 kiloNewtons. Determine Iso) of this rock. Predict the uniaxial compressive strength of this rock.
Problem No. 2 The above load-elongation data were obtained for a specimen with Lo = 0.1 m and ro 7 mm. Plot the stress-strain data and determine the E, G, and of Load (KN) 0.0 12.8 36.7 43.5 47.0 50.1 61.4 71.6 74.2 71.6 67.6 Elongation (mm) 0 0.0201 0.0690 0.1173 0.1898 0.2864 1.1684 3.5052 7.3025 10.2235 13.7287