You are given three metal test samples, with the same chemical composition and differing yield stresses sizes: A: 120.0, B: 140.0 and C: 160.0 MPa. Samples A and B have been microscopically examined and have grain sizes of 100 mm and 25 mm. Based on this information, which of the following values do you think will be the closest to the grain size of Sample C?

You are given three metal test samples, with the same chemical composition and differing yield stresses sizes: A: 120.0, B: 140.0 and C: 160.0 MPa. Samples A and B have been microscopically examined and have grain sizes of 100 mm and 25 mm. Based on this information, which of the following values do you think will be the closest to the grain size of Sample C?

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

You are given three metal test samples, with the same chemical composition and differing grain sizes: A: 5.0, B: 10.0 and C: 20.0 microns. Samples A and B have been tested and have yield stresses of 142.4 MPa and 135.8 MPa (all numbers are rounded off to the 1st decimal point). Based on this information, which of the following values do you think will be the closest to the yield stress of Sample C? In calculating the answer, use the Hall-Petch relation between yield stress of a metal ovield and the grain size of the metal d, which is Oyield = 00 + kd¯1/2 where k and og are constants. (This question has only one correct answer) a. 128.1 MPa O b. 115.8 MPa О с. 100.6 MPa O d. 131.1 MPa Ое. 152.4 MPa
Consider the tensile stress-strain diagram below. If samples 1 and 2 are identical except for the grain size, which sample has smaller grains? Note: This question will be marked negatively so consider your answer carefully. A. The samples have the same grain size B. Sample 1 C. Sample 2
In an engineering application, the material is a strip of iron with a fixed crystallographic structure subject to a tensile load during operation. The part failed (yielded) during operation and needs to be replaced with a component with better properties. You are told that two other iron strips had failed at yield stresses of 110 and 120 MPa, with grain sizes of 30 microns and 25 microns respectively. The current strip has a grain size of 20 microns. The diameter of the rod is 1 mm and the load applied is 100 N. What is the yield stress of the new part C and would you recommend it for operation? Select one: a. 140.5, no Ob. 129.5, yes OC. 120.5 MPa, no O d. 133.5 MPa, yes O e. 123.5 MPa, yes
In an engineering application, the material is a strip of iron with a fixed crystallographic structure subject to a tensile load during operation. The part failed (yielded) during operation and needs to be replaced with a component with better properties. You are told that two other iron strips had failed at yield stresses of 110 and 120 MPa, with grain sizes of 30 microns and 25 microns respectively. The current strip has a grain size of 20 microns. The diameter of the rod is 1 mm and the load applied is 100 N. What is the yield stress of the new part C and would you recommend it for operation? Select one: a.120.5 MPa, no b.140.5, no c.129.5, yes d.123.5 MPa, yes e.133.5 MPa, yes
In an engineering application, the material is a strip of iron with a fixed crystallographic structure subject to a tensile load during operation. The part failed (yielded) during operation and needs to be replaced with a component with better properties. You are told that two other iron strips had failed at yield stresses of 110 and 120 MPa, with grain sizes of 30 microns and 25 microns respectively. The current strip has a grain size of 20 microns. The diameter of the rod is 1 mm and the load applied is 100 N. What is the yield stress of the new part C and would you recommend it for operation? Select one: a. O b. 129.5, yes C. 133.5 MPa, yes e. 120.5 MPa, no d. 140.5, no 123.5 MPa, yes
In an engineering application, the material is a strip of iron with a fixed crystallographic structure subject to a tensile load during operation. The part failed (yielded) during operation and needs to be replaced with a component with better properties. You are told that two other iron strips had failed at yield stresses of 110 and 120 MPa, with grain sizes of 30 microns and 25 microns respectively. The current strip has a grain size of 20 microns. The diameter of the rod is 1 mm and the load applied is 100 N. What is the yield stress of the new part C and would you recommend it for operation?
O The following engineering stress-strain data were obtained for a 0.2% C plain-carbon steel. (i) Plot the engineering stress-strain curve. (ii) Determine the ultimate tensile strength of the alloy. (iii) Determine the percent elongation at fracture. Engineering Engineering Engineering Engineering Stress Strain Stress Strain (ksi) (in./in.) (ksi) (in./in.) 76 0.08 30 0.001 75 0.10 55 0.002 73 0.12 60 0.005 69 0.14 68 0.010 65 0.16 72 0.020 56 0.18 74 0.040 51 0.19 75 0.060 (Fracture)
Draw two schematic graphs using pencil showing a typical stress-strain curve for aluminum. The first graph should show engineering stress vs engineering strain, and the second graph should show true stress vs true strain. Label the showing: (i) elastic modulus (ii) proportional limit (iii) yield stress (iv)yield strain (v) fracture stress (vi) fracture strain on each graph. You may showboth graphs on one plot. Explain the difference between engineering stress and true stress.
Following is the Tensile stress-strain data for several hypothetical metals to be used. Answer the following questions referring to table 1.1. Table 1.1: Material Property Data Material Tensile Strength Fracture Strength Strain at Strength (MPa) (MPa) 340 265 550 505 112 150 Fracture before yielding A B C D 0.23 0.15 0.40 a. Which will experience the greatest percent reduction in area? Why? b. Which is the strongest? Why? c. Which is the stiffest? Why? Elastic Modulus (GPa) 210 310 180 400
Using the values found in the previous two questions, use the Hall-Petch equation and the graph below for a 70 Cu-30 Zn cartridge brass to predict the yield strength (in MPa) of this alloy when the average grain diameter is 1.0 x 10³ mm. Enter only the numerical value, do not include the unit. Grain size, d (mm) 10- 10-2 5 x 103 200 150 100 50 4 8. 12 16 d1/2 (mm-1/2) Yield strength (MPa)
The yield strength for an alloy that has an average grain diameter of 5.3 x 10 146 MPa. At a grain diameter of 7.8 × 10-3 mm, the yield strength increases to 249 MPa. At what grain diameter, in mm, will the yield strength be 236 MPa? d = Ex 0.0022 mm Check Try again 1
Q(4): Fill in the blanks of the following (Only Ten) 1. The stress and strain of a sample under mechanical testing can be classified into two types ------ and ------. 2. Dislocations in the real crystal can be classified into two groups based on their geometry it is ------ and ----- 3. Interstitial imperfection will act as a face resistance for moving of - ----- making it difficult to create permanent deformation in metals and alloys. 4. The error function of Erf (-x), is equal to 5. At the yield point or the proportional limit point, the deformation in this region is of the type ----- 6. There are two type of vacancy mechanism for atomic diffusion ---- -- and ------. 7. In no steady-state diffusion, the and the ----- at some particular point in a solid vary with time. 8. If exciton is localized, it is known as ------, and if it extends along a large number of repeating molecule units, then it is known as the -- 9. Elastic limit can be defined as ---- 10. The diffusion coefficient for…