The materlal has a fracture toughness of 25.4 MNM2 a yield strength of 453 MPa and is subjected to a stress of 114 MPa. Calculate the total effective length of the crack You may assume that the crack is small in relation to the component slze, that Poisson's ratio is 0.32, and that the plastic zone is consistent between all crack configurations.

The materlal has a fracture toughness of 25.4 MNM2 a yield strength of 453 MPa and is subjected to a stress of 114 MPa. Calculate the total effective length of the crack You may assume that the crack is small in relation to the component slze, that Poisson's ratio is 0.32, and that the plastic zone is consistent between all crack configurations.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

An airplane part is to be designed from view point of Fracture Toughness for which two materials are available. Consider Y=1.2 and ow =400 MPa, calculate (a) maximum internal crack length under the given condition for each material type. (b) How much stress on Aluminum part can be increased/decreased to comply with the critical crack length of 3 mm. 1/2 Кіс, МPa m Aluminum (7075-T3) 30 Titanium Ti-6AI-4Va 55
Help me please
A structural component in the shape of a flat plate 24.2 mm thick is to be fabricated from a metal alloy for which the yield strength and plane strain fracture toughness values are 537 MPa and 28.2 MPa-m¹/2, respectively. For this particular geometry, the value of Y is 1.9. Assuming a design stress of 0.4 times the yield strength, calculate the critical length of a surface flaw. i mm
The manufacturer of a product that is subjected to repetitive cycles has specified that the product should be removed from service when any crack reaches 15% of the critical crack length required to cause fracture. Consider a crack that is initially 0.02 mm long in a material with a fracture toughness of 55 MPaÖ The product is continuously cycled between compressive and tensile stresses of 300 MPa at a constant frequency. Assume external cracks for which f=1.12. The materials constant for these units are n = 3.4 and C= 2 X 10-11. What is the critical crack length required to cause fracture? How many cycles will cause product failure?
A material has a yield strength of 1150Mpa and a fracture toughness of 47 Mpa m^1/2. If the applied stress is 0.3 of the yield strength.Find the size of an internal crack that can lead to failure.
A component made of 7075-T6 aluminum alloy has an edge crack of 1.4 mm in length. Plane strain fracture toughness of this alloy is given as 27 MPavm. Geometrical factor of the crack is given as 1.2. (a) If this alloy is subjected to uniaxial tensile stress of 380 MPa, determine whether sudden brittle fracture occurs or not. (b) Calculate the maximum allowable crack size for this component in order not to be failed in brittle manner under a stress of 1000 MPa (Density of steel 7.85 g/cm³, 9.80665 N = 1 kg). Modulus of elastisity, GPa Ultimate tensile Yield strength, Alloy strength, MPa MPa 2014 Al alloy Bronze (92Cu-8Sn) High carbon steel Pure Titanium 97 186 380 72 110 152 380 615 215 240 330 107
A component made of 7075-T6 aluminum alloy has an edge crack of 1.4 mm in length. Plane strain fracture toughness of this alloy is given as 27 MPaym. Geometrical factor of the crack is given as 1.2. (a) If this alloy is subjected to uniaxial tensile stress of 380 MPa, determine whether sudden brittle fracture occurs or not. (b) Calculate the maximum allowable crack size for this component in order not to be failed in brittle manner under a stress of 1000 MPa
A large plate is fabricated from a steel alloy that has a plane strain fracture toughness of 55 MPa√m. If during service use, the plate is exposed to a tensile stress of 200 MPa, compute the minimum length of a surface crack that will lead to a fracture. Assume the value of 1.0 for Y.
Draw the stress strain diagram for a ductile and brittle material and what is the difference in it? What do you understand by strain hardening? What do you mean by percentage reduction in area? Explain the steps in ductile fracture. Explain the modes of failure in tension test.
A metal with an internal crack is loaded with a tensile stress of 20 MPa. If the crack length and the radius of curvature are 3.6 x 10-2 mm and 1.8 x 10-4 mm, compute its maximum stress. Given that the modulus of elasticity of the metal is 100 GPa and the specific surface energy is 3.5 J/m², compute its critical stress.
A mechanical component is fabricated from a metallic alloy. From the experiment, it is obtained that the fracture of this material occured at a stress of 36 ksi when the maximum internal crack length is 0.10 in. The plain strain fracture toughness of this material is 30 ksi sqrt(in) for this same component and alloy, investigate whether fracture will occur at stress level of 55 ksi when the internal crack length is 0.06 in.
The part of the vehicle is production from an magnesium alloy ,if KIC 40 MPa√m. The fracture occurred at a pressure of 195 MPa when the maximum edge crack length was 3.0 mm. Calculate the value Y. If a stress level is increased to 275 MPa and the maximum edge crack length is reduced to 2.3 mm, predict whether any fracture will occur. Compare your answer with existing data. Justify your answer