gineering / Civil Engineering/ Q&A Library /1a. a. During a tensile test on a speci... l a. During a tensile test on a specimen the following results were obtainc. Load (kN) 15 30 40 50 55 60 Extension (mm) 1.03 2.00 2.73 3.42 3.80 4.10 Diameter of gauge length =19mm Gauge length = 150mm Load at fracture- 80KN Diameter at fracture -16.Smm Gauge length at fracture - 170mm Ultimate load-120KN Plot the load/extension graph to an appropriate scale. Hence determine the i Modulus of elasticity ii. Percentage elongation iii. Percentage reduction in area iv. The nominal stress at fracture

gineering / Civil Engineering/ Q&A Library /1a. a. During a tensile test on a speci... l a. During a tensile test on a specimen the following results were obtainc. Load (kN) 15 30 40 50 55 60 Extension (mm) 1.03 2.00 2.73 3.42 3.80 4.10 Diameter of gauge length =19mm Gauge length = 150mm Load at fracture- 80KN Diameter at fracture -16.Smm Gauge length at fracture - 170mm Ultimate load-120KN Plot the load/extension graph to an appropriate scale. Hence determine the i Modulus of elasticity ii. Percentage elongation iii. Percentage reduction in area iv. The nominal stress at fracture

Steel Design (Activate Learning with these NEW titles from Engineering!)

6th Edition

ISBN:9781337094740

Author:Segui, William T.

Publisher:Segui, William T.

Chapter1: Introduction

Section: Chapter Questions

Problem 1.5.1P

See similar textbooks

Similar questions

A tensile test was performed on a metal specimen having a circular cross section with a diameter 0. 510 inch. For each increment of load applied, the strain was directly determined by means of a strain gage attached to the specimen. The results are, shown in Table: 1.5.1. a. Prepare a table of stress and strain. b. Plot these data to obtain a stress-strain curve. Do not connect the data points; draw a best-fit straight line through them. c. Determine the modulus of elasticity as the slope of the best-fit line.
A tensile test was performed on a metal specimen with a diameter of 1 2 inch and a gage length (the length over which the elongation is measured) of 4 inches. The dam were plotted on a load-displacement graph. P vs. L. A best-fit line was drawn through the points, and the slope of the straight-line portion was calculated to be P/L =1392 kips/in. What is the modulus of elasticity?
A tensile test was performed on a metal specimen having a circular cross section with a diameter of 1 2 inch. The gage length (the length over which the elongation is measured) is 2 inches. For a load 13.5 kips, the elongation was 4.6610 3 inches. If the load is assumed to be within the linear elastic rang: of the material, determine the modulus of elasticity.
Question 1 a) A standard mild steel tensile test specimen has a diameter of 16mm and a gauge length of 80mm. the specimen was tested to destruction and the following results obtained, Load at yield point = 87KN Extension at yield point = 173 x 10“ m Ultimate load = 124KN %3D Total extension at fracture = 24mm Diameter of specimen at fracture = 9.8mm Cross-sectional area at fracture = 75.4mm? Cross-sectional area "A" = 200mm² Compute the followings: Modulus of elasticity of steel. Ultimate tensile stress. i. ii. iii. Yield stress iv. Percentage elongation.
Question: A structural component in the form of a wide plate is to be fabricated from a steel alloy that has a plane strain fracture toughness of 98.9 MPa sqrt(m) (90 ksi sqrt(in.)) and a yield strength of 860 MPa (125,000 psi). The flaw size resolution limit of the flaw detection apparatus is 3.0 mm (0.12 in.). If the design stress is one-half of the yield strength and the value of Y is 1.0, determine whether or not a critical flaw for this plate is subject to detection.
The (G-E) diagram obtained in the tensile test performed on a metal sample with a diameter of 16 mm is as follows. The loads at points A, B and C and the elongation measured on l. 16 cm gauge length were determined as follows: B A B C Load (kgf) 4800 8400 7200 Elongation (mm) 0.192 28.8 38.4 c) Calculate the fracture work and the maximum elastic energy the metal rod can store. d) Find the cross-sectional area of a 6 m long rod made of this metal such that it can carry 12 tons of load with 2 times the safety of yield strength. How long does the rod extend under this load?
During a tensile test on a specimen of steel the following data was recorded, diameter of specimen 6.6mm gauge length of 50mm ,elongation of a load of 6.0 KN of 0.043mm. Reduction of area at failure of 45percent. Calculate the youngs modulus of elasticity ,the yield stress and the ultimate stress
Q7/ To test the splitting tensile strength (fct), the applied load (p) on the specimen was 150 kN, the tensile strength is..............
A steel bar with a 30 mm diameter is tested in tension. By monitoring the load reading of the testing machine, it was found that the specimen yielded at a load of 185 kN and fractured at 215 kN.a. Determine the tensile stresses at yield and at fracture.b. Estimate how much increase in length would occur at 70% of the yieldstress in a 50 mm gauge length.
A steel specimen is tested in tension. The specimen is 1 in. wide by 0.5 in. thick in the test region. By monitoring the load dial of the testing machine, it was found that the specimen yielded at a load of 36 kips and fractured at 48 kips.a. Determine the tensile stress at yield and at fracture.b. If the original gauge length was 4 in., estimate the gauge length when the specimen is stressed to 1/2 the yield stress.
Noncontact deformation measuring technique is preferred in many situations.
160 Upper scale A tensile test specimen of stainless steel alloy having a diameter of 0.550 in. and a gage length of 2.5 in. was tested to fracture. Stress and strain data obtained during 120 80 Lower scale the test are shown in the Figure Determine: (a) the modulus of elasticity. (b) the proportional limit. (c) the ultimate strength. (d) the yield strength (0.20% offset). (e) the fracture stress. 40 0.020 0.002 0.100 0.120 0.010 0.012 0.0 0.040 0.004 0.060 0.006 0.080 0.008 0.0 Strain (in./in.) Stress (ksi)