Elastic Properties of Materials4. A cylindrical bar of steel 10 mm (0.4 in.) in diameter is to be deformed elastically byapplication of a force along the bar axis. Using the data in Table given below, determinethe force that will produce an elastic reduction of 3 × 10¯³mm (1.2 × 10-4 in.) in thediameter.Metal AlloyAluminumBrassCopperMagnesiumNickelSteelTitaniumTungstenModulus ofElasticityGPa699711045207207107407106 psi1014166.5303015.559Shear ModulusGPa25374617768345160106 psi3.65.46.72.511.012.06.523.2Poisson's Ratio0.330.340.340.290.310.300.340.28

Answered: Image /qna-images/answer/ae5da957-bf95-45e7-bb1e-7b5b1540255d.jpg

Elastic Properties of Materials 4. A cylindrical bar of steel 10 mm (0.4 in.) in diameter is to be deformed elastically by application of a force along the bar axis. Using the data in Table given below, determine the force that will produce an elastic reduction of 3 x 10-³mm (1.2 × 10-4 in.) in the diameter.

Elastic Properties of Materials 4. A cylindrical bar of steel 10 mm (0.4 in.) in diameter is to be deformed elastically by application of a force along the bar axis. Using the data in Table given below, determine the force that will produce an elastic reduction of 3 x 10-³mm (1.2 × 10-4 in.) in the diameter.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Use the engineering stress strain diagram provided below to answer parts (A) to (H) below (the stress-strain diagram bas already been drawn for you): stress strain diagram 400 350 0 300 0 250 0 200 0 150.0 100.0 50.0 O 05 0 1 0.15 strain A. Determine the tensile strength of this alloy. B. show the elastic, plastic and total strain on the diagram stress (Mpa)
Determine the tensile yield strength (0.2% offset) and the maximum strength of a metal alloy having the following tensile stress-strain diagram. Tensile stress-strain diagram 150 100 0.05 02 05 035 Strain 300 250 200 150 100 50 W Stress (Mpa)
2) Use the engineering stress strain diagram provided below to answer parts (A) to (H) below (the stress-strain diagram has already been drawn for you): stress strain diagram 400 350 0 300 0 250 0 200 0 150.0 100.0 50.0 00 0 05 01 0. 15 strain A. Determine the tensile strength of this alloy. B. show the clastic, plastic and total strain on the diagram stress (Mpa)
Determine the tensile yield strength (0.2% offset) and the maximum strength of a metal alloy having the following tensile stress-strain diagram. Select one: The tensile yield strength Sy = 100 Mpa and the maximum strength Smax = 250 Mpa. The tensile yield strength Sy = 170 Mpa and the maximum strength Smax = 250 Mpa. The tensile yield strength Sy = 150 Mpa and the maximum strength Smax = 200 Mpa. The tensile yield strength Sy = 240 Mpa and the maximum strength Smax = 250 Mpa. The tensile yield strength Sy = 80 Mpa and the maximum strength Smax = 250 Mpa.
A tensile force of 200 KN is applied on a 0.02-m diameter and.2-m long rod. After applying the load, the diameter of the rod decreases to 0.01998 m and the length increases to 2.01 m. Assuming no permanent deformation occurs in that material, the modulus of elasticity (GPa) is?
Problem 4 The attached figure shows, for a gray cast iron, the tensile engineering stress-strain curve in the elastic region. Determine (a) the tangent modulus at 25 MPa and (b) the secant modulus taken to 35 MPa. Stress (MPa) 60 50 40 30 20 10 0.0002 0.0004 Strain 0.0006 T 8 6 ★ 2 0.0008 Stress (10³ psi)
you have a alloy. it has a 75GPa elastic moduls and it has been determined to have 215MPa of yeild strength. if your material has linear elastic stress-strain, figure out what the modulus of resiliance is for your alloy in J/m^3.
A hypothetical metal has an elastic behavior that follows Hook's law (o = Eɛ) and a plastic behavior that is best described by the following expression: a = -130,023ɛ² + 17,763ɛ + 660.26, where o is in MPa. Furthermore, plastic deformation occurs between strain values 0.0040 and 0.1150, beyond which fracture occurs. Determine the following: a. Modulus of elasticity (GPa) b. Yield strength at strain offset of 0.002 (MPa) Ultimate tensile strength (MPa) C. d. Brinell Hardness e. Resilience (J/m³) f. Ductility (%EI) g. Toughness (T/m³) h. True stress at fracture (MPa)
A bar having a length of 125 mm and cross-sectional area of 467.5 mm? is subjected to an axial force of 40 kN as shown in (Figure 1). Part A If the bar stretches 0.03 mm, determine the modulus of elasticity of the material. The material has linear-elastic behavior. Express your answer to three significant figures and include the appropriate units. HA Figure E = Value GPa Submit Request Answer Provide Feedback 40 kN 40 kN 125 mm
A tensile test is conducted on a mild steel bar. The following data was obtained from the test : diameter of the steel bar= 3cm, Gauge Length of the bar = 20cm, Load at Elastic limit= 250kN, Extension at a load of 150kN= 0.21 mm, Maximum Load = 380kN, Total Extension= 60mm, Diameter of the rod at failure=2.25cm, determine young's modulus?
(a) Two different materials designated A, and B, are tested in tension using test specimens having diameters of 0.505 cm and gage lengths of 2.0 cm (Figure 1). At failure, the distances between the gauge length marks are 2.13 cm (sample A) and 2.48 cm (sample B). Also, at the failure cross-sections, the diameters are found to be 0.484 cm (sample A) and 0.398 cm (sample B), respectively. Classify each material as brittle or ductile using your judgement.
A cylindrical bar of steel 10.4 mm (0.4094 in.) in diameter is to be deformed elastically by application of a force along the bar axis. Determine the force that will produce an elastic reduction of 3.3 x103 mm (1.299 x104 in.) in the diameter. For steel, values for the elastic modulus (E) and Poisson's ratio (v) are, respectively, 207 GPa and 0.30. i