A cylindrical specimen of undeformed brass that has a diameter of 300 mm is elastically deformed to a tensile strain of 0.001. If thePoisson's ratio for this brass is O.35, what is the change in specimen diameter?O Decrease by 3.00 x 104 mO Decrease by 1.05 x 104 mO Increase by 1.05 x 104 mO Increase by 0.028 mm

Answered: Image /qna-images/answer/e5d0a44d-24e5-4169-b180-76ed858211be.jpg

A cylindrical specimen of undeformed brass that has a diameter of 300 mm is elastically deformed to a tensile strain of 0.001. If the Poisson's ratio for this brass is 0.35, what is the change in specimen diameter? O Decrease by 3.00 x 10-4 m O Decrease by 1.05 x 10-4 m O Increase by 1.05 x 10-4 m O Increase by 0.028 mm

A cylindrical specimen of undeformed brass that has a diameter of 300 mm is elastically deformed to a tensile strain of 0.001. If the Poisson's ratio for this brass is 0.35, what is the change in specimen diameter? O Decrease by 3.00 x 10-4 m O Decrease by 1.05 x 10-4 m O Increase by 1.05 x 10-4 m O Increase by 0.028 mm

Materials Science And Engineering Properties

1st Edition

ISBN:9781111988609

Author:Charles Gilmore

Publisher:Charles Gilmore

Chapter6: Introduction To Mechanical Properties

Section: Chapter Questions

Problem 6.16P

See similar textbooks

Similar questions

The results of a tensile test are shown in Table 1.5.2. The test was performed on a metal specimen with a circular cross section. The diameter was 3 8 inch and the gage length (The length over which the elongation is measured) was 2 inches. a. Use the data in Table 1.5.2 to produce a table of stress and strain values. b. Plot the stress-strain data and draw a best-fit curve. c. Compute the, modulus of elasticity from the initial slope of the curve. d. Estimate the yield stress.
Question No.2 Figure P1.16 shows the stress-strain relations of metals A and B during ten- sion tests until fracture. Determine the following for the two metals (show all calculations and units): a. Proportional limit b. Yield stress at an offset strain of 0.002 m/m. c. Ultimate strength d. Modulus of resilience e. Toughness f. Which metal is more ductile? Why? 000 -Metal A S 600 -Metal B 300 0.00 a.02 0.04 0.06 0.08 0.10 0.12 0.14 Strain, mim FIGURE P1.16 Stress, MPa
A specimen of steel has a rectangular cross section 20 mm wide and 40 mm thick, an elastic modulus of 207 GPa, and a Poisson's ratio of 0.30. If this specimen is pulled in tension with a force of 60,000 N, what is the change in width if deformation is totally elastic? O Increase in width of 3.62 x 10-6 m O Decrease in width of 7.24 x 10-6 m Increase in width of 7.24 x 106 m O Decrease in width of 2.18 x 10-6 m
S Figure P1.16 shows the stress-strain relations of metals A and B during ten- sion tests until fracture. Determine the following for the two metals (show all calculations and units): a. Proportional limit b. Yield stress at an offset strain of 0.002 m/m. c. Ultimate strength d. Modulus of resilience e. Toughness f. Which metal is more ductile? Why? 900 Metal A 600 Metal B 300 0.00 0.02 0.04 0.06 0.08 0.10 0.12 0.14 Strain, m/m FIGURE P1.16 Stress, MPa
Question No.2 Figure P1.16 shows the stress-strain relations of metals A and B during ten- sion tests until fracture. Determine the following for the two metals (show all calculations and units): a. Proportional limit b. Yield stress at an offset strain of 0.002 m/m. c. Ultimate strength d. Modulus of resilience e. Toughness I. Which metal is more ductile? Why? 900 -Metal A E 600 Metal B 300 0.00 a02 004 a.06 0.08 0.10 0.12 014 Strain, matm FIGURE P1.16 Strees, MPa
A copper rod is deformed using a uniaxial tensile force of 16000 N. Deformation continues until sufficient strain hardening has occurred such that the applied force is too small to allow further deformation. After deformation, the rod has a diameter of 0.01 m and a length of 1.5 m. Assume that copper follows the strain hardening lawwith K of 310 MPa and n=0.54 Please calculate the true strain after the deformation ?
The elastic portion of the tension stress-strain diagram for an aluminum alloy is shown in the figure. The specimen used for the test has a gauge length of 2 in. and a diameter of 0.5 in. If the applied load is 10 kip, determine the new diameter of the specimen. The shear modulus is G al =3.811032 ksi
Figure P1.16 shows the stress–strain relations of metals A and B during tension tests until fracture. Determine the following for the two metals (show all calculations and units): Proportional limit Yield stress at an offset strain of 0.002 in./in. Ultimate strength Modulus of resilience Toughness Which metal is more ductile? Why?
Q1/ Consider the brass alloy for which the stress-strain behavior is shown in the figure below. A cylindrical specimen of this material 10.0 mm in diameter and 101.6 mm long is pulled in tension with a force of 10,000 N. If it is known that this alloy has a value for Poisson's ratio of 0.35, compute (a) the specimen elongation, and (b) the reduction in specimen diameter. 500 70 Tensile strength 450 MPa (65,000 psi) 60 400 50 10 psi 300 MPa 40 40 30 200 Yield strength 30 200 250 MPa (36,000 psi) 20 100 20 10 100 10 0.005 0.10 0.20 0.30 0.40 Strain Stress (MPa) Stress (10 psi)
Strain = 600 Stress = Strain = 500 Stress = 400 500 300 400 300 200 200 100 100 0.000 0.002 0.004 0.006 Strain 0.00 0.04 0.08 0.12 0.16 0.20 Strain Stress (MPa)
An aluminum specimen originally 300 mm long is pulled in tension with a stress of 275 MPa. If the deformation is entirely elastic, what will be the resultant elongation? The aluminum modulus of elasticity is 75 GPa. 4.13
A 5-mm-thick rectangular alloy bar is subjected to ajtensile load P by pins at A and B, as shown in the figure. The width of the bar is w = 33 mm. Strain gages bonded to the specimen measure the following strains in the longitudinal (x) and transverse (y) directions: €, =710 με and ε,--255 με (a) Determine Poisson's ratio for this specimen. (b) If the measured strains were produced by an axial load of P = 24 kN, what is the modulus of elasticity for this specimen? Answers: (a) v= (b) E= GPa