a) 6 kilograms of iron-carbon steel structure that consists of 99.55wt.% Fe and 0.45wt. C is slowly cooled down from 1100°C to just below 727°C. By using the existing phase diagram of an iron-carbon system as given in Figure Q2(a), analysis the phase of the alloy at the selected temperatures of: a) 1100°C b) 750°C c) 727°C + 4T d) 727°C – AT The phase analysis must include phase present, chemical composition of the phases, amounts of each phase in grams and microstructure.

a) 6 kilograms of iron-carbon steel structure that consists of 99.55wt.% Fe and 0.45wt. C is slowly cooled down from 1100°C to just below 727°C. By using the existing phase diagram of an iron-carbon system as given in Figure Q2(a), analysis the phase of the alloy at the selected temperatures of: a) 1100°C b) 750°C c) 727°C + 4T d) 727°C – AT The phase analysis must include phase present, chemical composition of the phases, amounts of each phase in grams and microstructure.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

XCu versus temperature, liquid-solid phase- equilibrium diagram of a system consisting of Ag and Cu is given. a) Identify each zone and point O b) Define the temperatures T1, T2 and T3 c) Find the degrees of freedom for the points R, T, U, V and Y (f).
Consider 1 kg of tin-bismuth alloy (Sn-Bi) containing 40 wt% Bi. The phase diagram of the alloy is shown in the figure below. The alloy is cooled to 138 "C (just below the eutectic temperature). How many kilograms of phase B form? 300 271°C 232°C 200 Bi + L В +L 139 C 21 100 Bi - В + Bi 13°C vate Windows 100gs to activate Windows (Bi) 20 40 60 80 (Sn) 6:37 PM A 4) ENG 57 B. Temperature (°C)
Consider 1 kg of Sn-Bi alloys, and how many kilograms each phase forms according to the condition given in the below figure. a) L 0.66: Alpha 0.34 kg b) L 0.69: Alpha 0.31 kg c) L 0.74: Alpha 0.26 kg d) L 0.34: Alpha 0.66 kg
Q1/ A simplified portion of the iron carbon equilibrium diagram is shown below.a) Name the phase in the areas 1,2,3,4,5,6 and 7 on the diagram. b) what type of reaction occurs at 723'C? state the condition of the reaction and write the equation of the reaction. 900 800 700-> 600-> 500 400 300 200- 100-> 0.8 1.0 .Carbon Temperature "C
An Ag-Cu alloy contains 25% a and 75% B at 600°C. The composition of the overall alloy is approximately 1000 L+B 800 8-87 28-12 922 a + B 500 972 400 Ag 10 20 30 40 50 60 70 80 90 Cu %Cu (by weight) A. 80.2% Cu B. 73.5% Cu C. 65.8% Cu D. 89.6% Cu
The Lead-Tin phase diagram: a) Show the eutectic three phase reaction on this phase diagram. b) A Pb-45% Sn alloy is cooled from 300°C to 100°C. What phases are present for this alloy at this temperature range? What is the composition of the phases? How much of each phase is present? c) Calculate the amount of eutectic mixture for Pb-45% Sn alloy at 100°C. d) What is the alloy composition (Pb-x% Sn), which has a microstructure of 60% Eutectic mixture and 40% ß phase at 100°C. Composition (at% Sn) 20 40 60 80 100 327°C H600 300 Liquid 500 232°C a + L 200 B +L 400 183°C 18.3 61.9 97.8 300 100 a + B H200 H100 20 40 60 80 100 (Рb) Composition (wt% Sn) (Sn) Temperature ("C) Temperature (°F)
The phase diagram of the alloy Copper – Silver is shown in the figure below. Composition (at% Ag) 20 100 2200 40 60 80 1200 2000 A -Liquidus 1000 Liquid 1800 -Solidus F a +L 779°C (Tg). 1600 B+L 9 800 E B G 91.2 (Cog 8.0 71.9 1400 1200 600 1000 Solvus a +B 800 400 C 600 H 200 0 60 400 100 20 40 80 (Cu) Composition (wt% Ag) (Ag) (a) Cite the phases that are present and the phase compositions for the following alloys: 1) 5 wt% Cu – 95 wt% Ag at 900 °C 2) 50 wt% Cu – 50 wt% Ag at 1000°C 3) 30 wt% Cu – 70 wt% Ag at 900 °C 4) 20 wt% Cu - 80 wt% Ag at 600 °C 5) 40 wt% Cu – 60 wt% Ag at 600 °C (b) Determine the eutectic temperature and eutectic composition. (c) What is the maximum solubility of silver in copper and at which temperature? Temperature ("C) Temperature ("F)
Consider Al- Cu system below. When Al-40%Cu is heated above 600°C and cooled slowly to a temperature of 545°C . Answer the following. Use the values of composition given in the phase diagram , no estimation .Each has two marks. 700 1200 600 L a + L 6 +L 548 1000 500 (CUAL) a + 6 800 400 600 300 5.65 10 20 30 32.7 40 50 52.5 (AI) Composition (wt % Cu) a. Percentage of the pro-eutectic phase present (% no decimal places) b. Composition of the pro- eutectic phase present (in %Cu one decimal place) c. What is the percentage of larger eutectic component present (% no decimal places) Temperature (°C) Temperature (°F)
help pls A two-phase phase diagram is shown. Answer the following questions t -1300 1500+ Temperature 1100 0 34 54! 166 482 80 Composition of Ni % 20 What is the composition (in % Cu) of the solid phase corresponding to the red dot in between the solidus and liquidus lines in the phase diagram? Just write the number. Do not write the % symbol. Question 17 2.33 100 An alloy is being made with 66% Ni and 34% Cu. When it is cooled from 1500°C to the temperature corresponding to the red dot in the phase diagram, how many kg of liquid is present in the mixture?
For the equilibrium silver-copper system, if you were at a temperature of 779°C and a composition of 60 wt% Cu, what fraction of the system would be in the a phase? Your answer should be in the form of a percentage (a value 0-100). °C 1084.5 1000 961.93 900 a +L B+L 800 780 80 71.9 91.2 700 600 a+B 500 400 Cu 10 20 30 40 50 60 70 80 90 Ag Weight Percent Silver
A Pb-30% Sn alloy is cooled from 300°C to 50°C. a) What phases are present for this alloy at 50°C? b) How much of each phase is present at 50°C? c) What is the primary phase and its amount for this alloy at 50°C? Composition (at% Sn) 20 40 60 80 100 327°C 600 300 Liquid 500 232°C a + L 200 ß + L 400 183°C 18.3 61.9 97.8 300 100 a + B 200 100 40 60 80 100 (Pb) Composition (wt% Sn) (Sn) Temperature (°C) 20 Temperature (°F)
A) Identify all congruent reactions and their coordinates in the phase diagramB) Identify all invariant reactions (reaction type and coordinates) in the phase diagramC) Starting from a liquid at 70 at.% Ni and 1800 degrees C, cool the liquid slowly such that thermodynamic equilibrium is always maintained.C1) At what temperature does solid first appear?C2) Identify the solid phase which appears first from the liquid state and its approximate compositionC3) At what temperature does the liquid finally disappear?C4) What is the liquid composition when it finally disappearsC5) Identify the last solid phase which appears during cooling and the temperature at which this last solid phase appearsC6) At the point where the last solid phase appears during cooling, identify the phases present, give their compositions, and calculate their fractions