Compression molding is a manufacturing process in which the molding material is preheated then placed in an open mold cavity where thecompressive action of the punch forces the polymer into the desired shape as shown in the figure below. Based on your understanding of thebehavior of polymers, which of the statements below regarding compression molding of polymers are accurate?PunchCavityC.-Upper mold halfCharge41(1)-Lower mold halfKnock-out pinV, F|x.F(2) and (3)Molded parta. Lower operating temperatures are more desirable as they reduce viscosity making it easier to fill the cavityb. This process can only be used for thermosets as they can thermally cure from monomer stateThis process can be used for both thermosets and thermoplastics as they can both be thermally shapedd. This process is suitable for rubber, PVC and polymethyl methacrylate

Compression molding process is used to give a desired shape to the plastic with the use of high…

Compression molding is a manufacturing process in which the molding material is preheated then placed in an open mold cavity where the compressive action of the punch forces the polymer into the desired shape as shown in the figure below. Based on your understanding of the behavior of polymers, which of the statements below regarding compression molding of polymers are accurate? Punch Cavity (1) Charge Upper mold half Lower mold half Knock-out pin (2) and (3) Molded part P ☐a. Lower operating temperatures are more desirable as they reduce viscosity making it easier to fill the cavity b. This process can only be used for thermosets as they can thermally cure from monomer state ☐ c. This process can be used for both thermosets and thermoplastics as they can both be thermally shaped Od. This process is suitable for rubber, PVC and polymethyl methacrylate

Compression molding is a manufacturing process in which the molding material is preheated then placed in an open mold cavity where the compressive action of the punch forces the polymer into the desired shape as shown in the figure below. Based on your understanding of the behavior of polymers, which of the statements below regarding compression molding of polymers are accurate? Punch Cavity (1) Charge Upper mold half Lower mold half Knock-out pin (2) and (3) Molded part P ☐a. Lower operating temperatures are more desirable as they reduce viscosity making it easier to fill the cavity b. This process can only be used for thermosets as they can thermally cure from monomer state ☐ c. This process can be used for both thermosets and thermoplastics as they can both be thermally shaped Od. This process is suitable for rubber, PVC and polymethyl methacrylate

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

The 3D printing approach shown below is fused deposition modelling (FDM), where feedstock polymer is fed into the heated printer nozzle and deposited onto the platform to form the final object in the desired geometry. Which of the polymers below are suitable for this process and what nozzle temperature should be used for that material? Z AXIS X AXIS HOME Y AXIS D LEGEND: A : Extruder B: Nozzle C: Printed part D: Hot plate E: Filament Select one or more: a. Polyvinyl chloride - 110°C (for PVC: Tg = 120°C, Tmelt = 240°C, HDT = 92 °C) b. ABS-125°C (for ABS: Tg = 140°C, Tmelt = 200°C, HDT = 100 °C) c. Polyvinyl chloride - 250°C (for PVC: Tg = 120°C, Tmelt = 240°C, HDT = 92 °C) d. ABS-215°C (for ABS: Tg = 140°C, Tmelt = 200°C, HDT = 100 °C)
You are injection molding plastic gears. Where would you place the gate (injection point) and Why? Be sure to consider polymer chain orientation, which is determined by the gate location, and how it affects the mechanical properties of the injection molded gears. 5
Q5 (a) Figure 6 shows two types of polymeric products fabricated using different processing techniques. Suggest with justification for the type of processes used to produce the products: i. Product A ii. Product B A B Figure 6. Two types of polymeric products (a) plastic bottles and (b) plastic car boot tray (b) The molecular weight data of a Polymer X are given in Table 3. Once undergone a melting process, it achieves degree of polymerization, DP of 498 upon solidification. i. Calculate the number-average molecular weight (Mn) for the polymer. ii. Calculate the molecular weight for monomers of the Polymer X. iii. Prove that the Polymer X is a polytetrafluoroethylene (PTFE) with chemical formula of (C2F4)n- Given the atomic weights for carbon, C is 12.011 g/mol and fluorine, F is 18.998 g/mol.
(b) Which of the following plastic and composite materials processing is most suitable for the application of polymer automotive body panel? Explain how the selected manufacturing process selected can be used to produce the product shown in Figure 1.2 below • Injection Moulding • Reaction injection Moulding (RIM) • Blow Moulding • Rotational Moulding • Thermoforming • Compression Moulding (CM) • Transfer Moulding (TM) • Casting • Foam Moulding SULIT SULIT (BMCG 2323) Figure 1.2 Example of polymer automotive body panel
A manufacturer would like to produce carbonated beverage plastic bottle which requires good precision and mechanical properties. Identify with supported explanation in terms of process characteristics which polymer processing method is suitable for this application. (Word limit: ~120)
A manufacturer plant to produce a new thermoplastic product. Select a suitable processing method that can be applied А. Transfer moulding В. Rotating moulding C. Compression moulding D. Casting
Please make sure to display your thought process? It is imperative to be able to follow how the answer was deduced. Please be as thorough as possible. Please address all parts of this question as they are all part and critical to answering this question correctly. Please show good integrity when answering the question: Strain-rate, temperature, pressure, and aging time all affect the stress/strain behavior of polymers. Draw a stress-strain curve below for a typical ductile polymer. Clearly label the yield point and the ultimate tensile strength. Using this curve draw two new curves corresponding to same polymer but now tested at: 1) an increase in temperature and 2) an increase in strain rate. Explain what happens to the tensile behavior after: a) a prolong time of aging time is increased and b) when the tensile tests are conducted under super imposed hydrostatic compression
Injection molding is a process in which a polymer is heated to a highly plastic state and forced to flow under high pressure into a mold cavity, where it solidifies and is then removed from the cavity: O true O false
Molecular weight data for some polymer are tabulated here. Compute (a) the number-average molecular weight, (b) the weight-average molecular weight. (c) If it is known that this material's degree of polymerization is 710, which one of the polymers listed in Table 14.3 is this polymer? Why? Molecular Weight Range g/mol 15,000-30,000 Xi Wi 0.04 0.01 30,000-45,000 0.07 0.04 45,000-60,000 0.16 0.11 60,000-75,000 0.26 0.24 75,000-90,000 0.24 0.27 90,000 105,000 0.12 0.16 105,000-120,000 0.08 0.12 120,000-135,000 0.03 0.05
Page 12 of 13 4. Give TWO (2) examples of polymers that can used as a resin in mounting process. 1. 2. 5.Fill in the blank with the following: [grain boundary, dislocation, coarse, stronger] A fine-grained material (one that has small grains) is harder and that is area to impede than one -grained, because the former has a greater total movement. 6. Label ferrite and pearlite in the following photomicrographs of a PCS specimen. 7. Which one is coarser? ANS: (a) Abrasive paper: 180 grit paper or 320 grit paper ANS: (b) Metal specimen: ASTM grain-size number; 4 or 10
A stress of 1000 psi is applied to a polymerthat operates at a constant strain; after sixmonths, the stress drops to 850 psi. For aparticular application, a part made of thesame polymer must maintain a stress of900 psi after 12 months. What should bethe original stress applied to the polymerfor this application?
When a polymer takes on a crystalline structure, its density, stiffness, and melting temperature decrease. T or F