Answered: 1. A bracket is shown in the figure.…

1. A bracket is shown in the figure. Calculate the stresses on the welding. The bracket welded by E7018 clectrode. Based on stresses calculations, calculate the design factor of safety

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Te - Effective throat thickness well in mm = 6 sin45° Consider the following drawing in which plate 1 is welded onto plate 2 as shown for tensile and shear loading. The plates are fillet welded with a weld thickness of 6 mm as shown for a length of 150 mm. The plates have an ultimate strength of 275 MPa and the welding was done with F70 welding electrodes, which possesses an ultimate strength of 483 MPa. Consider a partial factor of safety of 1.7 for the welded joint and determine the design strength of the weld joint, both in tension (Tdw) and in shear (Vdw) due to the forces acting on it. a) Determine the design strength of the following weld in tension ( ) due to vertical forces. b) Determine the design strength of the weld in shear ( ) due to horizontal forces. Attached pic is shear equation for calculation Tension equation for calculation is: Tdw = FyLwte /Ymw
Mechanical Design Ch9: Welded Joints 9-29 The permissible shear stress for the weldment illustrated is 140 MPa. Estimate the load, F, that will cause this stress in the weldment throat. 3rd year - Mechanical. Engineering. Problem 9-29 6 mm 200 mm 75 mm
4. A solid shaft was made of alloy steel, it was welded to a flat plate by a specific size of fillet weld. If a torque is applied to the shaft, calculate the size of the weld joint. Power Torque Yield stress Shear stress Ultimate stress (Mpa) Compression stress (Mpa) Ductility (%) (kw) (Nm) 1000 (Mpa) 400 (Mpa) 160 280 30 Modulus of Bending Stress Bending Moment Factor of Safety Elasticity (GPa) (Mpa) 220 280 120 4 Modulus of Rigidity (pa) 70 Fracture stress (Mpa) 250
(6) The weldment shown in the figure is subjected to an alternating force F. The hot-rolled steel bar is 10 mm thick and is of AISI 1010 steel. The vertical support is likewise of 1010 steel. The electrode is 6010. Estimate the fatigue load F the bar will carry if three 6-mm fillet welds are used. (22.1 kN) 50 60 Dimensions in millimeters
The weldment shown in Figure 2 is subjected to an alternating force F. The hot-rolled steel bar is 10 mm thick and is of AISI 1010 steel. The vertical support is likewise of 1010 steel. The electrode is 6010. (a) Estimate the fatigue load F the bar will carry if three 6-mm fillet welds are used. 6. 6 50 F -60 Dimensions in millimeters
The carrier plate material St52 (S355) given in the figure below is welded to the body. combined. F1 = 4 kN and F2 = 40 kN static forces act on the plate. Source I. Quality (v2 = 1), no impact (v3 = 1), weld thickness a = 5 mm, safety coefficient s = 2 and weld seam coefficient v1 = 0.8 will be taken. Find out whether a = 5 mm weld seam thickness is sufficient or not, according to the data in the figure and above.
The weldment shown in the figure is subjected to a force F. The hot-rolled steel bar has a thickness h and is of AISI 1040 steel. The vertical support is likewise AISI 1040 HR steel. The electrode is given in the table below. Estimate the static load F the bar can carry if two fillet welds are used. b (mm) h (mm) d (mm) 70 Elecrode E8010 30 6 F
3.) The diagram below shows a 5.5m long double angle brace which is connected by 6mm welding connection. The length of weld shown in the picture is 300 mm on the top and 100 mm on the bottom. The 2-L127x 89x6.4 are 300W steel and long leg back-to-back. The braces are to be welded to a 12 mm 350W steel gusset plate. Determine the factored tensile capacity of the angles. Any intermediate connections that are required should also be specified. 740 kN -12 mm Gusset Plate
The weldment shown in the figure is subjected to a static force of 100 kN. The hot-rolled steel bar has a thickness h=6 mm and is of AISI 1015 HR steel. The vertical support is AISI 1015 HR steel. The electrode is given in the table below. Use the welding code method. (a) is the weld metal strength satisfactory? (b) Is the attachment strength satisfactory? h h=6 mm b=60 mm d=90mm electrode=E6010 |-b- h F
9-25 The weldment shown in the figure is subjected to an alternating force F. The hot-rolled steel to bar has a thickness h and is of AISI 1010 steel. The vertical support is likewise AISI 1010 HR 9-28 steel. The electrode is given in the table below. Estimate the fatigue load F the bar will carry if three fillet welds are used. Problem Number b 9-25 9-27 50 mm 50 mm d 50 mm 5 mm 30 mm 5 mm h Electrode E6010 E7010 |-b Problems 9-25 to 9-28
Q1: The weldment shown in the figure is subjected to a force F. The hot-rolled steel bar has a thickness h and is of AISI 1040 steel. The vertical support is likewise AISI 1040 HR steel. The electrode is given in the table below. Estimate the static load F the bar can carry if two fillet welds are used. b (mm) d (mm) h (mm) Elecrode E8010 30 70 6 ko →→ F
Q1: The weldment shown in the figure is subjected to a force F. The hot-rolled steel bar has a thickness and is of AISI 1040 steel. The vertical support is likewise AISI 1040 HR steel. The electrode is given in the table below. Estimate the static load F the bar can carry if two fillet welds are used. h (mm) b (mm) 30 d (mm) 70 Elecrode E8010